Reaction | p, % [4] | Еγ, keV [5] | γ-abn, % [5] | T1/2, d [5] | DL, % | tcool, day | tmeas, min |
23Na(n,γ)24Na | 100 | 1368.6 | 100 | 0.62 | 1.2 × 10−5 | 6 | 30 |
45Sc(n,γ)46Sc | 100 | 1120.54 | 99.99 | 83.79 | 1.3 × 10−8 | 40 | 167 |
50Cr(n,γ)51Cr | 4.34 | 320.08 | 10.08 | 27.70 | 1.2 × 10−4 | 40 | 167 |
58Fe(n,γ)59Fe | 0.28 | 1099.24 | 56.5 | 44.50 | 3.7 × 10−5 | 40 | 167 |
59Co(n,γ)60Co | 100 | 1173.23 | 99.85 | 1925.3 | 2.9 × 10−7 | 40 | 167 |
64Zn(n,γ)65Zn | 48.63 | 1115.54 | 50.70 | 243.9 | 6.3 × 10−6 | 40 | 167 |
75As(n,γ)76As | 100 | 559.10 | 45 | 1.09 | 4.1 × 10−6 | 10 | 30 |
94Zr(n,γ)95Zr | 17.38 | 756.70 | 54.5 | 64.02 | 1.5 × 10−4 | 40 | 167 |
109Ag(n,γ)110mAg | 48.16 | 884.68 | 72.7 | 249.76 | 3.4 × 10−6 | 40 | 167 |
123Sb(n,γ)124Sb | 42.79 | 1690.97 | 47.79 | 60.20 | 1.1 × 10−5 | 40 | 167 |
133Cs(n,γ)134Cs | 100 | 795.86 | 85.45 | 754.31 | 3.6 × 10−7 | 40 | 167 |
139La(n,γ)140La | 99.91 | 1596.21 | 95.4 | 1.68 | 1.2 × 10−7 | 6 | 30 |
140Ce(n,γ)141Ce | 88.45 | 145.44 | 48.3 | 32.51 | 5.84 × 10−5 | 40 | 167 |
141Pr(n,γ)142Pr | 100 | 1575.8 | 3.7 | 0.80 | 1.59 × 10−4 | 3 | 30 |
151Eu(n,γ)152Eu | 47.81 | 1408.01 | 21.07 | 4944.4 | 7.8 × 10−8 | 40 | 167 |
152Gd(n,γ)153Gd | 0.20 | 97.43 | 29.0 | 240.40 | 6.89 × 10−2 | 40 | 167 |
159Tb(n,γ)160Tb | 100 | 966.17 | 25.1 | 72.30 | 8.7 × 10−8 | 40 | 167 |
186W(n,γ)187W | 28.43 | 685.73 | 27.3 | 0.99 | 7.6 × 10−6 | 6 | 30 |
232Th(n,γ)233Th | 100 | 311.90 | 38.5 | 26.98 | 4.3 × 10−4 | 40 | 167 |